ASTM-A262 › Historical Revision Information
Standard Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels
Show Complete Document History
The following bibliographic material is provided to assist you with your purchasing decision:
This specification covers the standard practices for detecting susceptibility to intergranular attack in austenitic stainless steels. These practices include five intergranular corrosion tests, namely: (1) oxalic acid etch test for classification of etch structures of austenitic stainless steels; (2) ferric sulfate-sulfuric acid test, (3) nitric acid test and (4) copper-copper sulfate-sulfuric acid test for detecting susceptibility to intergranular attack in austenitic stainless steels; and (5) copper-copper sulfate-50% sulfuric acid test for detecting susceptibility to intergranular attack in molybdenum-bearing cast austenitic stainless steels. Methods for preparing the test specimens, rapid screening tests, apparatus setup and testing procedures, and calculations and report contents are described for each testing practice. The etch structure types used to classify the specimens are: step structure, dual structure, ditch structure, isolated ferrite, interdendritic ditches, end-grain pitting I, and end-grain pitting II.
Scope
1.1 These practices cover the following five tests:
1.1.1 Practice A—Oxalic Acid Etch Test for Classification of Etch Structures of Austenitic Stainless Steels (Sections 3 to 7, inclusive),
1.1.2 Practice B—Ferric Sulfate–Sulfuric Acid Test for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels (Sections 8 to 14, inclusive),
1.1.3 Practice C—Nitric Acid Test for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels (Sections 15 to 21, inclusive),
1.1.4 Practice E—Copper–Copper Sulfate–Sulfuric Acid Test for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels (Sections 22 to 31, inclusive), and
1.1.5 Practice F—Copper–Copper Sulfate–50 % Sulfuric Acid Test for Detecting Susceptibility to Intergranular Attack in Molybdenum-Bearing Austenitic Stainless Steels (Sections 32 to 38, inclusive).
1.2 The oxalic acid etch test is a rapid method of identifying, by simple etching, those specimens of certain stainless steel grades that are essentially free of susceptibility to intergranular attack associated with chromium carbide precipitates. These specimens will have low corrosion rates in certain corrosion tests and therefore can be eliminated (screened) from testing as “acceptable.” The etch test is applicable only to those grades listed in the individual hot acid tests and classifies the specimens either as “acceptable” or as “suspect.”
1.3 The ferric sulfate–sulfuric acid test, the copper–copper sulfate–50 % sulfuric acid test, and the nitric acid test are based on weight loss determinations and, thus, provide a quantitative measure of the relative performance of specimens evaluated. In contrast, the copper–copper sulfate–16 % sulfuric acid test is based on visual examination of bend specimens and, therefore, classifies the specimens only as acceptable or nonacceptable.
1.4 The values stated in SI units are to be regarded as standard. The inch-pound equivalents are in parentheses and may be approximate.
1.5 This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. (Specific precautionary statements are given in 5.6, 11.1.1, 11.1.9, and 35.1.)
Keywords
austenitic stainless steel; copper sulfate; corrosion testing; etch structures; ferric sulfate; intergranular corrosion; nitric acid; oxalic acid; ICS Number Code 77.140.20 (Steels of high quality)
To find similar documents by ASTM Volume:
01.03 (Steel--Plate, Sheet, Strip, Wire; Stainless Steel Bar)
To find similar documents by classification:
This document comes with our free Notification Service, good for the life of the document.
This document is available in either Paper or PDF format.
Document Number
ASTM-A262-13
Revision Level
2013 EDITION
Status
Superseded
Modification Type
Revision
Publication Date
June 1, 2013
Document Type
Practice
Page Count
17 pages
Committee Number
A01.14