Standard Test Method for Flow Rates for Poly(Vinyl Chloride) with Molecular Structural Implications

Show Complete Document History

Document Center Inc. is an authorized dealer of ASTM standards.
The following bibliographic material is provided to assist you with your purchasing decision:

Standard Test Method for Flow Rates for Poly(Vinyl Chloride) with Molecular Structural Implications


1.1 This test method is an extension of Test Method D1238 specific to the measurement of flow rates of poly(vinyl chloride) (PVC) compounds while detecting and controlling various polymer instabilities associated with the flow rate.

1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to inch-pound units that are provided for information only and are not considered standard.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Note 1—There is no known ISO equivalent to this standard.

Significance and Use

This test method is useful for quality-control tests on PVC compounds having a wide range of melt viscosities. Measurements are made at shear rates close to 1 s1.

In addition to the properties mentioned in Test Method D1238, this technique is sensitive to plasticizer content, polymer molecular weight, polymer stability (both thermally and rheologically), shear instability, and general composition. The sensitivity of the material to temperature necessitates slightly tighter controls than those stated in Test Method D1238.

The sensitivity of this test method makes it useful for correlating with processing conditions and as an aid in predicting changes in processing. However, as a one-point measure of flow relative to shear rate, its one drawback is that the same PVC melt flow values can be obtained for materials having different processibility; the chance of this happening is minimized, however, if the compounds are similar in composition.

Correlations with a wide range of processing conditions have supported the conclusions that little or no change in composition occurs during the test. Thus, this test is able to detect and follow profound changes which occur during extrusion, injection molding, milling, or mixing. These changes are due to three types of measured instability in polymers:

Thermal instability due to temperature effect.

Shear instability due to breaking of polymer bonds.

Rheological instability due to nonuniform distributions of widely different viscosity or molecular weight elements.

Thus, implications with respect to PVC molecular structural changes can be detected and predicted.


chain shearing; crosslinking; degradation; fragmentation; melt flow rate; poly(vinyl chloride); rheology; shear instability: Crosslinking; Degradation--plastics; Flow and flow rate--thermoplastics; Melt flow rate (of thermoplastics); Poly(vinyl chloride)(PVC); Shear instability; ICS Number Code 83.080.20 (Thermoplastic materials)

To find similar documents by ASTM Volume:

08.02 (Plastics (II): D3222 - D5083)

To find similar documents by classification:

83.080.20 (Thermoplastic materials)

This document comes with our free Notification Service, good for the life of the document.

This document is available in either Paper or PDF format.

Document Number


Revision Level

1999 R11 EDITION



Modification Type


Publication Date

Oct. 1, 2011

Document Type

Test Method

Page Count

5 pages

Committee Number