ASTM-A516 › Historical Revision Information
Standard Specification for Pressure Vessel Plates, Carbon Steel, for Moderate- and Lower-Temperature Service
Show Complete Document History
The following bibliographic material is provided to assist you with your purchasing decision:
Scope
1.1 This specification covers carbon steel plates intended primarily for service in welded pressure vessels where improved notch toughness is important.
1.2 Plates under this specification are available in four grades having different strength levels as follows:
Tensile Strength, | |
Grade U.S. [SI] | ksi [MPa] |
55 [380] | 55-75 [380-515] |
60 [415] | 60-80 [415-550] |
65 [450] | 65-85 [450-585] |
70 [485] | 70-90 [485-620] |
1.3 The maximum thickness of plates is limited only by the capacity of the composition to meet the specified mechanical property requirements; however, current practice normally limits the maximum thickness of plates furnished under this specification as follows:
Maximum Thickness, | |
Grade U.S. [SI] | in. [mm] |
55 [380] | 12 [305] |
60 [415] | 8 [205] |
65 [450] | 8 [205] |
70 [485] | 8 [205] |
1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.
Keywords
pressure vessel steel materials-plates; steel plate-carbon steel; welding/welds-steel plate/sheet/strip; pressure vessel plates-carbon steel, for moderate-/lower-temperature
To find similar documents by ASTM Volume:
01.04 (Steel--Structural, Reinforcing, Pressure Vessel, Railway)
To find similar documents by classification:
This document comes with our free Notification Service, good for the life of the document.
This document is available in either Paper or PDF format.
Document Number
ASTM-A516/A516M-90(1996)e1
Revision Level
1990 R96(E1) EDITION
Status
Superseded
Modification Type
Editorially changed
Publication Date
Dec. 28, 1990
Document Type
Specification
Page Count
3 pages
Committee Number
A01.11