ASTM-B160 › Historical Revision Information
Standard Specification for Nickel Rod and Bar
The following bibliographic material is provided to assist you with your purchasing decision:
This specification covers nickel (UNS N02200), low carbon nickel (UNS N02201), and solution strengthened nickel (UNS N02211) in the form of hot-worked, cold-worked, or annealed rods and bars of round, square, hexagonal, or rectangular solid section. The material shall conform to the chemical composition limits specified for nickel, copper, iron, manganese, carbon, silicon, and sulfur. Mechanical requirements including tensile strength, yield strength, and elongation are given for specific conditions and diameter or distance between parallel surfaces. Chemical analysis, tension test, and hardness test shall be performed.
Scope
1.1 This specification covers nickel (UNS N02200)*, low carbon nickel (UNS N02201)*, and solution strengthened nickel (UNS N02211) in the form of hot-worked and cold-worked rod and bar in the conditions shown in Table 1.
1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.
TABLE 1 Mechanical Properties
Condition and Diameter or Distance Between Parallel Surfaces, in. (mm) | Tensile Strength, min, psi (MPa) | Yield Strength (0.2 % offset), min. psi (MPa)A | Elongation in 2 in. or 50 mm or 4D, min % |
---|---|---|---|
Nickel (UNS N02200) | |||
Cold-worked (as worked): | |||
Rounds, 1 (25.4) and under | 80 000 (550) | 60 000 (415) | 10B |
Rounds over 1 to 4 (25.4 to 101.6) incl. | 75 000 (515) | 50 000 (345) | 15 |
Squares, hexagons, and rectangles, all sizes | 65 000 (450) | 40 000 (275) | 25B |
Hot-worked: | |||
All sections, all sizes | 60 000 (415) | 15 000 (105) | 35C |
Rings and disksD | — | — | — |
Annealed: | |||
Rods and bars, all sizes | 55 000 (380) | 15 000 (105) | 40B |
Rings and disksE | — | — | — |
Forging quality | |||
All sizes | F | F | F |
Low-Carbon Nickel (UNS N02201) and Solution Strengthened Nickel (UNS N02211) | |||
Hot-worked: | |||
All sections, all sizes | 50 000 (345) | 10 000 (70) | 40C |
Annealed: | |||
All products, all sizes | 50 000 (345) | 10 000 (70) | 40B |
A See 12.2.
B Not applicable to diameters or cross sections under 3/32 in. (2.4 mm).
C For hot-worked flats 5/16 in. (7.9 mm) and under in thickness the elongation shall be 25%, min.
D Hardness B45 to B80, or equivalent.
E Hardness B45 to B70 or equivalent.
F Forging quality is furnished to chemical requirements and surface inspection only. No tensile properties are required.
Keywords
bar; rod; N02200; N02201; N02211; Nickel--specifications; Nickel alloy rod/bar/wire--specifications; UNS N02200 (commercially pure Ni alloy, Nickel 200); UNS N02201 (commercially pure Ni alloy, Nickel 201); ICS Number Code 2211; 77.150.40 (Nickel and chromium products)
To find similar documents by ASTM Volume:
To find similar documents by classification:
77.120.40 (Nickel, chromium and their alloys)
77.150.40 (Nickel and chromium products)
This document comes with our free Notification Service, good for the life of the document.
This document is available in either Paper or PDF format.
Document Number
ASTM-B160-05e1
Revision Level
2005(E1) EDITION
Status
Superseded
Modification Type
Editorially changed
Publication Date
Oct. 1, 2008
Document Type
Specification
Page Count
6 pages
Committee Number
B02.07