Scope

1.1 This test method covers the determination of density for powder metallurgy (PM) materials containing less than two percent porosity and for cemented carbides. This test method is based on the water displacement method.

Note 1—A test specimen that gains mass when immersed in water indicates the specimen contains surface-connected porosity. Unsealed surface porosity will absorb water and cause density values higher than the true value. This test method is not applicable if this problem occurs.

1.2 With the exception of density values, for which the g/cm³ unit is the industry standard, the values stated in SI units are to be regarded as the standard. Values in inch-pound units are shown in parentheses and result from conversion in accordance with IEEE/ASTM Standard SI 10.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Significance and Use

For PM materials containing less than two percent porosity, a density measurement may be used to determine if the part has been densified, either overall or in a critical region, to the degree required for the intended application. Density alone cannot be used for evaluating the degree of densification because chemical composition and heat treatment affect the pore-free density.

For cemented carbides, a density measurement is normally used to determine if there is any significant deviation in composition of the carbide grade. For straight tungsten carbide-cobalt grades, the relationship is straightforward. For complex carbide grades (for example, grades containing tantalum carbide or titanium carbide, or both, in addition to tungsten carbide-cobalt), the situation is more complicated. If the measured density is beyond the specified limits, the composition is outside of the specified limits. A measured density within the specified limits does not ensure correct composition; compensation between two or more constituents could result in the expected density with the wrong composition. Density alone cannot be used for evaluating a cemented carbide grade.

Keywords

cemented carbides; density; hard metals; metal injection molded (MIM) parts; powder metallurgy (P/M); powder forged (P/F) parts; powder metallurgy; ICS Number Code 77.160 (Powder metallurgy)

To find similar documents by ASTM Volume:

02.05 (Metallic and Inorganic Coatings; Metal Powders and Metal Powder Products)

To find similar documents by classification:

77.160 (Powder metallurgy Including sintered metal materials and hardmetals)

This document comes with our free Notification Service, good for the life of the document.

This document is available in either Paper or PDF format.