ASTM-C874 › Historical Revision Information
Standard Practice for Rotary Slag Testing of Refractory Materials
The following bibliographic material is provided to assist you with your purchasing decision:
Scope
1.1 This test method describes a procedure for comparing the behavior of refractories to the action of molten slag in a rotating test furnace. A reference material should be included in each test and run for comparison. No numeric results are obtained from this test method. Numeric evaluation of test results is the responsibility of the test operator. The test and equipment are patterned after a method developed by Valley Dolomite Corporation .
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Significance and Use
This test method outlines a procedure which, when appropriate evaluation methods are added, can be useful in the development of new products or in the selection of products to be used in contact with a particular slag composition.
A gradient exists through the test specimens that is controlled by the thermal conductivity of the specimens and backup material. The slag is constantly renewed so that a high rate of corrosion is maintained. The flow of the slag can cause mechanical erosion of materials. The tilt and rotational speed of the furnace will affect the amount of mechanical erosion.
Use caution in interpreting results when materials of vastly different types are included in a single run. Care must be taken to prevent oxidation of carbon-containing materials during heat up; failure to do so can result in highly erratic results. A reference refractory specimen, or specimens, should be used for comparison.
Keywords
corrosion; penetration; refractories; rotary; slag; Refractories (general); Rotary slag testing; Slag
To find similar documents by ASTM Volume:
15.01 (Refractories, Activated Carbon; Advanced Ceramics)
To find similar documents by classification:
81.080 (Refractories Including ceramic refractories)
This document comes with our free Notification Service, good for the life of the document.
This document is available in either Paper or PDF format.
Document Number
ASTM-C874-11
Revision Level
2011 EDITION
Status
Superseded
Modification Type
Revision
Publication Date
Feb. 1, 2011
Document Type
Practice
Page Count
3 pages
Committee Number
C08.04