ASTM-A811 › Historical Revision Information
Standard Specification for Soft Magnetic Iron Parts Fabricated by Powder Metallurgy (P/M) Techniques

ASTM-A811 - 2003 EDITION - SUPERSEDED
Show Complete Document History

Document Center Inc. is an authorized dealer of ASTM standards.
The following bibliographic material is provided to assist you with your purchasing decision:


This specification covers soft magnetic iron parts fabricated by powder metallurgy (P/M) techniques. The material shall conform to the chemical composition requirements. The density of P/M parts is determined by the compressibility of the powder, the compacting pressure, and sintering practice (temperature, time, and atmosphere). The magnetic property evaluation procedures for P/M parts are presented. Three grades, defined by coercive field strength are presented; Grade 3 was developed from interlaboratory study, Grades 2 and 3 are based on a literature review and are believed to reflect the current industry capabilities. A lot shall consist of parts of the same form and dimensions, produced from a single mixed powder batch and from an unchanged process, without discontinuity in production, and submitted for inspection at one time.

ORDER

Scope

1.1 This specification covers parts produced from iron powder metallurgy materials.

1.2 This specification deals with P/M parts in the sintered or annealed condition. Should the sintered parts be subjected to any secondary operation that causes mechanical strain, such as machining or sizing, they should be resintered or annealed.

1.3 The values stated in customary (cgs-emu and inch-pound) units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units which are provided for information only and are not considered standard.

Keywords

coercive field strength; iron; P/M parts; powder metallurgy (P/M); ICS Number Code 77.160 (Powder metallurgy)

To find similar documents by ASTM Volume:

03.04 (Magnetic Properties)

To find similar documents by classification:

77.160 (Powder metallurgy Including sintered metal materials and hardmetals)

This document comes with our free Notification Service, good for the life of the document.

This document is available in either Paper or PDF format.

Document Number

ASTM-A811-03

Revision Level

2003 EDITION

Status

Superseded

Modification Type

Revision

Publication Date

May 10, 2003

Document Type

Specification

Page Count

4 pages

Committee Number

A06.02